2000 SQM Capacity Fiber Cement Board Production Line for Heat Insulation Fire Fighting Sheets AIA-1 manufacturer from China Shandong Chuangxin Building Materials Complete Equipments Co., Ltd

2000 SQM Capacity Fiber Cement Board Production Line for Heat Insulation Fire Fighting Sheets

Place of Origin:

Guangdong, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: AIA-1

2000 SQM Capacity Fiber Cement Board Production Line for Heat Insulation Fire Fighting Sheets </di

2000 SQM Capacity Fiber Cement Board Production Line for Heat Insulation Fire Fighting Sheets

Automatic Line Fiber Cement Board Production Machine With 2000 SQM Capacity

Product Description

Fiber cement Board production line
Fiber cement board is made from Cement, quartz sand and certain amount of fiber. It is produced after several procedures such as pulp preparation, forming, autoclaving, drying, polishing and after-processing. It has advantages such as light in weight, high in strength, good in processing and easy in decorating, and it can also has performances of heat insulation and fire fighting. So it can be widely used in inner wall and suspended ceiling of buildings, sound panel and partition board partition board of gymnasium, theater and council chamber. It can also be used for special facilities in various industries, such as sound proof wall and apron plate of highway, permanent moulding board of constructional engineering, bay plate of train and ship, movable board for house and outer board of large-scale clad plate factory.
Fiber Cement Board is new environment-protection product with favorable market prospect and economic benefit.

Basic technical data
1. Product name: Non-asbestos fiber cement board
2. Standard: In conformity with National Building Material Industry Standard JC/T 412.1-2006. < Non-asbestos fiber cement board>
3. Raw material: Cement, reinforced fiber, coal ash additives
4. Product specification: ( L*W*T) 2440× 1220× 6-30mm
5. Capacity: 3 million -5million /year( calculate by 2440× 1220× 6mm board, 24 working hours continous production )
6. Production organization arrangement: 1) 3 shifts per day, 8 hours per shift, 300working days per year 2)total wokers need for this line is 52 staff, including 2 management staff, 2 techincal staff and 48 workers.
No. Test items Standard indicators Test results
1 Bending degrees
Horizontal > =22Mpa 24.9Mpa Qualified
Vertical > =17 Mpa 21.4Mpa
2 Impact strength > =2.0 KJ/m2 3.7KJ/m2 Qualified
3 Indensity > =1.6g/cm3 1.72g/cm3 Qualified
4 Water absorption < =24% 16.8% Qualified
5 Waterproofness According to the National standard GB8041 tested -24H checking allow damp mark on the back of the board, but no water drop Meet the National standard GB8041 Qualified
6 Freezing resistance According to the National standard GB8041 tested- after 25 times Cycliccrackingno break and layer appear Meet the National standard GB804

Compressive Strength	~20 MPa (3, 000 PSI)
Impact Resistance	> 6 kJ/m2
Tensile Strength	> 5.5 MPa
Density (Specific Mass)	~1000 Kg/m3 (+/-< 2%)
Moisture Absorption	~26% maximum saturation (slow absorption rate)
Moisture Content	~6%
Water Vapour Diffusion	~28 / 35
Specific Heat	~930 J/kgK
Thermal Conductivity	~0.44 W / mK
Modulus of elasticity	~6045 N/mm2
Flexibility UNI E 12372	~20.1 N/mm2 maximum 12mm x 1220 x 2440 = 10 N/mm2
Surface Alkalinity	~10 Ph
Thermal Expansion Hot/Cold	0, 01 mm/mC (from temp +20C to -20C)
Expansion in Water	less than < 0.02% from ambient to saturation
Freeze / Thaw - UNI EN 520	100 cycles without notable effects
Frost Resistance	no water drops form on surface
Combustibility / Fire Ratings	non-combustible / 12mm exceeds 1 hr fire rating
Dimensional tolerance	thick 0.2mm / width 2mm / length 3mm / Sq. 3mm
Toxicity Pollutants Heavy Metals - UNI EN 12457-2	Below measurable levels of test instruments
Asbestos Analysis	Absent - not measurable
Formaldehyde Analysis	Absent - not measurable
Sound Attenuation (9mm)	tested design ASTM E90 = STC 48, 50, 55, & 60
Color	Slate Grey and Chalk White
Surface texture	smooth one side; uniform machine textured back
Basic Compounds	(MgO)+(natural silicates)+(glass fibre)+(wood fibre)